316 standard plate hot rolled aisi steel
Introduction
316 stainless steel, 18Cr-12Ni-2.5Mo because adding Mo, so the corrosion resistance, weather resistance and high temperature strength in particular, in the harshness of the conditions of use; hardening excellent (non-magnetic).
Corrosion resistance than 304 stainless steel, in pulp and paper production process has good resistance to corrosion. And 316 stainless steel is also resistant to aggressive industrial marine and atmospheric erosion.
heat treatment. In the 1850-2050°F temperature range of annealing and then rapidly annealed and then rapidly cooled. 316 stainless steel can be hardened by heat treatment.
Welding 316 stainless steel has good weldability. All standard welding methods can be used for welding. Welding according to the application, were used 316Cb, 316L stainless steel or 309Cb filler rod or electrode welding. For optimum corrosion resistance, stainless steel welding section 316 require post-weld annealing. If you use 316L stainless steel, does not require post-weld annealing
| Artical | 316 standard plate hot rolled aisi steel | ||||||
| Specification | 1000mm*2000mm,1219mm*2438mm or as your requirement | ||||||
| Surface | no.1 | ||||||
| Type | plate | ||||||
| Thickness | 3mm~100mm | ||||||
| Mill | TISCO/ BAOSTEEL/ JISCO/ ZPSS | ||||||
| Packing | Standard export packing | ||||||
| Payment terms | 1.30%T/T in advance, the balance against the B/L copy | ||||||
| 2.30%T/T in advance, the balance against the L/C at sight | |||||||
| 3.100%L/C at sight | |||||||
| Dilivery time | 1.10days after receving the deposit of T/T | ||||||
| 2.10days after receving the L/C original | |||||||
chemical properties
| Typical chemical composition | ||||
| % | 304 | 304L | 316 | 316L |
| C | 0-0.07 | 0-0.03 | 0.8 | 0.03 |
| Mn | 0-2.0 | 0-2.0 | 2 | 2 |
| Si | 0-1 | 0-1 | 0.75 | 0.75 |
| P | 0-0.05 | 0-0.05 | 0.045 | 0.045 |
| S | 0-0.02 | 0-0.02 | 0.03 | 0.03 |
| Cr | 17.5-19.5 | 17.5-19.5 | 16.0-18.0 | 16.0-18.0 |
| Ni | 8-10.5 | 8-10.5 | 10.0-14.0 | 10.0-14.0 |
| Mo | 2.00-3.00 | 2.00-3.00 | ||
| N | 0.1 | 0.1 | ||
| Fe | Balance | Balance | ||
Pysical properties
Tensile strength σb (MPa) ≥ 520
Conditions yield strength σ0.2 (MPa) ≥ 205
Elongation δ5 (%) ≥ 40
Section shrinkage ψ (%) ≥ 60
Hardness: ≤ 187HB; ≤ 90HRB; ≤ 200HV
Surface
Pictures of products
(Pictures may be different from the actual,Please carefully read the instructions)
Packing
Application
316, Pulp and paper equipment heat exchangers, dyeing equipment, film processing equipment, pipelines, coastal areas outside the building materials used.2013 should also be in the field of the solenoid valve, mainly for housing, clamps, ball, valve, valve seat, nut, stem, etc